SPOT WELDING METHOD

Abstract:

Provided is a spot welding method by which welding can be successfully performed while inhibiting occurrence of expulsion. First to third metal plates W1 to W3 were welded in which ratio of total thickness to thickness of the first metal plate W1 is 7. In Example 1, peak current value A1 is 14.6 kA, effective current value A2 is 7.8 kA, peak duration T1 is 0 ms, and no-peak duration T2 is 5.9 ms. As a result, in Example 1, lower limit current value A3 is 6.9 kA, upper limit current value A4 is 8.42 kA, difference A5 between upper limit current value A4 and lower limit current value A3 is 1.52 kA, peak duration T1/no-peak duration T2 is 0, effective current value A2/peak current value A1 is 0.53, and rising time T3/falling time T4 is 0.79, furthermore, no expulsion occurs, and welding result was determined to be OK.